MAJORIS G401 - 7841/E

Polypropylene

AD majoris

长玻璃纤维

产品说明：

MAJORIS G401 - 7841/E is a special long glass fibre reinforced polypropylene grade, for injection moulding and extrusion. The long glass fibres, chemically coupled to the polypropylene matrix, are providing with outstanding mechanical properties.
This product is high heat distortion temperature stabilised.
MAJORIS G401 - 7841/E is available both in natural (MAJORIS G401) and black (MAJORIS G401 - 8229). Other colours can be provided on request.
APPLICATIONS
MAJORIS G401 - 7841/E is intended for injection moulding of highly demanding technical applications.
The excellent properties of MAJORIS G401 - 7841/E make it suitable for:

• Electrical components, automotive parts, interior, exterior and under the bonnet, structural furniture parts, load bearing, demanding components for various engineering sectors.

MAJORIS G401 - 7841/E can, in many of these applications, substitute other engineering plastics or metal alloys.

物性信息：

基本信息
填料/增强材料	长玻璃纤维
添加剂	热稳定剂
特性	化学耦合 可回收材料 耐热性，高 热稳定性
用途	电气元件 家具 金属取代 汽车的发动机罩下的零件 汽车内部零件 汽车外部零件
外观	黑色 可用颜色 自然色
形式	粒子
加工方法	挤出 注射成型

物理性能	额定值	单位制	测试方法
密度	1.24	g/cm3	ISO 1183
收缩率	0.40	%

机械性能	额定值	单位制	测试方法
拉伸模量	8800	MPa	ISO 527-2/1
拉伸应力 (断裂)	119	MPa	ISO 527-2/50
拉伸应变 (断裂)	2.2	%	ISO 527-2/50
弯曲模量	7850	MPa	ISO 178

冲击性能	额定值	单位制	测试方法
简支梁缺口冲击强度			ISO 179/1eA
-20°C	27	kJ/m2	ISO 179/1eA
23°C	24	kJ/m2	ISO 179/1eA
简支梁无缺口冲击强度 (23°C)	52	kJ/m2	ISO 179/1eU

热性能	额定值	单位制	测试方法
热变形温度 (0.45 MPa, 未退火)	162	°C	ISO 75-2/B
维卡软化温度	145	°C	ISO 306/B
线形热膨胀系数 - 流动			ASTM D696
-30°C	4.4E-5	cm/cm/°C	ASTM D696
23°C	3.1E-5	cm/cm/°C	ASTM D696

注射	额定值	单位制
料筒后部温度	230 到 250	°C
加工（熔体）温度	250 到 280	°C
模具温度	80.0 到 100	°C
注塑压力	30.0 到 60.0	MPa
注射速度	慢
螺杆转速	30 到 150	rpm

注射说明
Holding pressure: 50 to 70% of the injection pressureBack pressure: as low as possible, 0 to 10%Holding time: as long as practical