Total LDPE 1022 FH 24 Low Density Polyethylene - Blown Film

Low Density Polyethylene (LDPE), Film Grade

Total Atofina

产品说明：

LDPE 1022 FH 24 is a low density polyethylene made by a high pressure process.

LDPE 1022 FH 24 is a slip and anti-block formulated grade.

LDPE 1022 FH 24 is suited to many applications in the field of consumer, industrial, food or hygiene packaging such as bags, lamination and coextrusion film.

Information provided by Total Petrochemicals.

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	0.923 g/cc	0.923 g/cc	ISO 1183
厚度	40.0 microns	1.57 mil	for samples tested on this data sheet
	20.0 - 150 microns	0.787 - 5.91 mil	possible range, depending on extrusion conditions
熔体流动速率	2.3 g/10 min @Load 2.16 kg, Temperature 190 °C	2.3 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Antiblock Level	750 ppm	750 ppm	Talc
Slip Level	750 ppm	750 ppm	Erucamide

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度(MD : 屈服)	12.0 MPa	1740 psi	ISO 527-3
抗张强度(TD : 屈服)	11.5 MPa	1670 psi	ISO 527-3
断裂伸长率，MD	350 %	350 %	ISO 527-3
断裂伸长率，TD	580 %	580 %	ISO 527-3
埃尔曼多夫抗撕强度(MD)	7.30 g/micron	185 g/mil	ISO 6383-2
埃尔曼多夫抗撕强度(TD)	6.10 g/micron	155 g/mil	ISO 6383-2
落锤试验	95.0 g	0.209 lb	ISO 7765-1
抗张强度(MD : 断裂)	22.0 MPa	3190 psi	ISO 527-3
抗张强度(TD : 断裂)	20.0 MPa	2900 psi	ISO 527-3

热性能	额定值 (公制)	额定值 (英制)	测试方法
熔融温度	109 °C	228 °F	ISO 11357
维卡软化温度	94.0 °C	201 °F	ISO 306

光学性能	额定值 (公制)	额定值 (英制)	测试方法
雾度	8.0 %	8.0 %	ISO 14782

加工性能	额定值 (公制)	额定值 (英制)	测试方法
加工温度	150 - 190 °C	302 - 374 °F