| 品牌 | 美国陶氏 |
|---|---|
| 货号 | 321 |
| 牌号 | 9107 |
| 型号 | 9107 |
| 品名 | 其它工程塑料 |
| 外形尺寸 | 0.1 |
| 产品用途 | 可吹塑成薄膜用作一次性手套、医药和食品包装；挤塑制软管和型材；吹塑制玩具；发泡制泡沫板材等 。 |
| 生产企业 | 123 |
| 是否进口 | 是 |
INFUSE™ 9107
Olefin Block Copolymer
陶氏塑料
产品说明：
INFUSE™ 9107 Olefin Block Copolymer is a lower density higher performance olefin copolymer that can be widely used in TPE applications where higher service temperature requirements are needed. INFUSE 9107 also provides high filler loading capability and gives good elastic recovery.
Main Characteristics:
Complies with:
Main Characteristics:
- High upper service temperature performance
- Highly flexible with good elastic recovery
- Fast set up times for processability
- General purpose elastomer
- Excellent for compounds and blends
- Talc dusted
Complies with:
- EU, No 10/2011
- U.S. FDA FCN 424
物性信息：
| 基本信息 | |
|---|---|
| 机构评级 |
|
| 形式 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.866 | g/cm3 | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 A, 模压成型) | 60 | ASTM D2240 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 - 正割 (模压成型) | 1.61 | MPa | ASTM D638 |
| 抗张强度 (断裂, 模压成型) | 5.10 | MPa | ASTM D638 |
| 伸长率 (断裂, 模压成型) | 600 | % | ASTM D638 |
| 弹性体 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 (断裂) | 11.0 | MPa | ASTM D412 |
| 伸长率 (断裂) | 1600 | % | ASTM D412 |
| 撕裂强度 | 27.0 | kN/m | ASTM D624 |
| 压缩 变形 | ASTM D395 | ||
| 21°C | 16 | % | ASTM D395 |
| 70°C | 49 | % | ASTM D395 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 溶融温度（DSC） | 121 | °C | 内部方法 |
| TMA 1(1.00 mm) | 66 | °C | 内部方法 |
| 备注 | |
|---|---|
| 1 . | 1N，5°C/分 |