EMS-Grivory Grivory® HT2V-15H PA6T/66-GF15

Nylon 66/6, 20% Glass Fiber Reinforced

EMS-Grivory (EMS-CHEMIE)

产品说明：

Product description: Grivory HT2V-15H is a 15 % glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Polymer designation acc. to ISO: PA 6T/66 Acc. to ASTM: PPA, polyphthalamide The main distinguishing feature of Grivory HT, when compared to other polyamides, is its good performance at high temperatures providing parts which are stiffer, stronger and have better heat distortion stability and chemical resistance. Grivory HT is suitable for production of technical parts in the application fields of:

• Electro
• Electronics
• Automotive
• Safety technology
• Mechanical engineering

Information provided by EMS Grivory

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	1.29 g/cc	0.0466 lb/in3	ISO 1183
吸水率	6.0 %	6.0 %	ISO 62
水分吸收	2.00 %	2.00 %	ISO 62
线性成型收缩率,Flow	0.0050 cm/cm	0.0050 in/in	ISO 294-4, 2577
线性成型收缩率，横向	0.010 cm/cm	0.010 in/in	ISO 294-4, 2577

机械性能	额定值 (公制)	额定值 (英制)	测试方法
肖氏硬度 (邵氏 D)	87	87	conditioned, 15s; ISO 868
	88	88	dry, 15s; ISO 868
球压硬度	175 MPa	25400 psi	conditioned; ISO 2039-1
	210 MPa	30500 psi	dry; ISO 2039-1
抗张强度(断裂)	115 MPa	16700 psi	dry; ISO 527-1/-2
	115 MPa	16700 psi	conditioned; ISO 527-1/-2
伸长率 (断裂)	2.0 %	2.0 %	dry; ISO 527-1/-2
	2.0 %	2.0 %	conditioned; ISO 527-1/-2
拉伸模量	7.00 GPa	1020 ksi	conditioned; ISO 527-1/-2
	7.00 GPa	1020 ksi	dry; ISO 527-1/-2
简支梁无缺口冲击强度	2.50 J/cm2	11.9 ft-lb/in2	dry; ISO 179/1eU
	2.50 J/cm2	11.9 ft-lb/in2	conditioned; ISO 179/1eU
	2.50 J/cm2 @Temperature 30.0 °C	11.9 ft-lb/in2 @Temperature 86.0 °F	dry; ISO 179/1eU
	2.50 J/cm2 @Temperature 30.0 °C	11.9 ft-lb/in2 @Temperature 86.0 °F	conditioned; ISO 179/1eU
简支梁缺口冲击强度	0.500 J/cm2	2.38 ft-lb/in2	dry; ISO 179/1eA
	0.500 J/cm2	2.38 ft-lb/in2	conditioned; ISO 179/1eA
	0.500 J/cm2 @Temperature 30.0 °C	2.38 ft-lb/in2 @Temperature 86.0 °F	dry; ISO 179/1eU
	0.500 J/cm2 @Temperature 30.0 °C	2.38 ft-lb/in2 @Temperature 86.0 °F	conditioned; ISO 179/1eU

电气性能	额定值 (公制)	额定值 (英制)	测试方法
体积电阻率	1.00e+12 ohm-cm	1.00e+12 ohm-cm	dry; IEC 60093
	1.00e+12 ohm-cm	1.00e+12 ohm-cm	conditioned; IEC 60093
表面电阻	1.00e+12 ohm	1.00e+12 ohm	IEC 60093
介电强度	38.0 kV/mm	965 kV/in	dry; IEC 60243-1
	38.0 kV/mm	965 kV/in	conditioned; IEC 60243-1
相比耐漏电起痕指数(CTI)	500 V	500 V	conditioned; IEC 60112

热性能	额定值 (公制)	额定值 (英制)	测试方法
线形热膨胀系数 - 流动	30.0 μm/m-°C	16.7 μin/in-°F	ISO 11359-1/-2
线性热膨胀系数,横向流动	75.0 μm/m-°C	41.7 μin/in-°F	ISO 11359-1/-2
熔融温度	310 °C	590 °F	10°C/min; ISO 11357-1/-3
工作温度, Air	140 °C	284 °F	long term; EMS
	240 °C	464 °F	short term; EMS
载荷下热变形温度(1.8 MPa)	270 °C	518 °F	ISO 75-1/-2
载荷下热变形温度(8.0 MPa)	100 °C	212 °F	ISO 75-1/-2
可燃性(UL94)	HB	HB	IEC 60695-11-10

材料描述		测试方法
汽车	Exterior
	Fuel systems
	Interior
	Powertrain and Chassis
电器及电子产品	Connectors
形式	Granules
工业和消费品	Housewares
	Hydraulics & Pneumatics
	Mechanical Engineering
	Power transmission
	Sports & Leisure
	Tools & Accessories
加工	Injection Molding
特殊特性	Improved heat resistance
	Improved UV resistance (outdoor use)