Ineos ABS NOVODUR® P2L-AT ABS, Injection Grade

Acrylonitrile Butadiene Styrene (ABS), Molded

Ineos ABS

产品说明：

Injection molding grade, very easy flow, antistatic, high stiffness, high gloss.

Applications: Telephones, household goods, disk and video housings, office equipment.

Information provided by the manufacturer.

Novodur is produced by Styrolution (2014). This grade was discontinued prior to Styrolution's acquisition of the Novodur product line.

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	1.05 g/cc	0.0379 lb/in3
吸水率	0.30 %	0.30 %	Saturation in water
饱和吸水率	0.30 %	0.30 %
熔体流动速率	45 g/10 min @Load 10.0 kg, Temperature 220 °C	45 g/10 min @Load 22.0 lb, Temperature 428 °F

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度(屈服)	45.0 MPa	6530 psi
屈服伸长率	2.1 %	2.1 %
拉伸模量	2.70 GPa	392 ksi
简支梁无缺口冲击强度	7.00 J/cm2	33.3 ft-lb/in2
	0.350 J/cm2 @Temperature -30.0 °C	1.67 ft-lb/in2 @Temperature -22.0 °F
简支梁缺口冲击强度	1.00 J/cm2	4.76 ft-lb/in2

电气性能	额定值 (公制)	额定值 (英制)	测试方法
电阻率	1.00e+15 ohm-cm	1.00e+15 ohm-cm
表面电阻	1.00e+15 ohm	1.00e+15 ohm
介电常数	3.0 @Frequency 1e+6 Hz	3.0 @Frequency 1e+6 Hz
	3.1 @Frequency 100 Hz	3.1 @Frequency 100 Hz
介电强度	31.0 kV/mm	787 kV/in
耗散因数	0.0080 @Frequency 100 Hz	0.0080 @Frequency 100 Hz
	0.0080 @Frequency 1e+6 Hz	0.0080 @Frequency 1e+6 Hz
相比耐漏电起痕指数(CTI)	600 V	600 V

热性能	额定值 (公制)	额定值 (英制)	测试方法
线形热膨胀系数 - 流动	90.0 μm/m-°C @Temperature 20.0 °C	50.0 μin/in-°F @Temperature 68.0 °F
载荷下热变形温度(0.46 MPa)	96.0 °C	205 °F
载荷下热变形温度(1.8 MPa)	92.0 °C	198 °F
维卡软化温度	96.0 °C	205 °F
可燃性(UL94)	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in