Ineos ABS Lustran® LGA-SF

Acrylonitrile Butadiene Styrene (ABS), Molded

Ineos ABS

产品说明：

Key Features:

• Unfilled

Suitable processing methods:

• Injection molding

Information provided by Bayer Polymers.

LANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with Lanxess in 2007. Subsequently Ineos acquired of Ineos ABS.

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	1.06 g/cc	0.0383 lb/in3
熔体流动速率	25 g/10 min @Load 10.0 kg, Temperature 220 °C	25 g/10 min @Load 22.0 lb, Temperature 428 °F	cm3/10 min.

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度(屈服)	40.5 MPa	5870 psi
伸长率 (断裂)	26 %	26 %	Nominal
屈服伸长率	3.4 %	3.4 %
拉伸模量	2.13 GPa	309 ksi
简支梁缺口冲击强度	2.10 J/cm2	9.99 ft-lb/in2
	0.650 J/cm2 @Temperature -30.0 °C	3.09 ft-lb/in2 @Temperature -22.0 °F

热性能	额定值 (公制)	额定值 (英制)	测试方法
线形热膨胀系数 - 流动	92.0 μm/m-°C @Temperature 20.0 °C	51.1 μin/in-°F @Temperature 68.0 °F
载荷下热变形温度(0.46 MPa)	87.0 °C	189 °F
载荷下热变形温度(1.8 MPa)	74.0 °C	165 °F
维卡软化温度	94.0 °C	201 °F	50°C/h 50N

加工性能	额定值 (公制)	额定值 (英制)	测试方法
加工（熔体）温度	250 °C	482 °F	Injection Molding
模具温度	60.0 °C	140 °F	Injection Molding
射速	200 mm/sec	7.87 in/sec
注射压力	55.0 MPa	7980 psi