Proto3000 ABS-M30 Fused Deposition Modeling Polymer

Rapid Prototyping Polymer

Proto3000

产品说明：

Description: ABS-M30 is up to 25-70 percent stronger than standard Stratasys ABS and is an ideal material for conceptual modeling, functional prototyping, manufacturing tools, and end-use-parts. ABS-M30 has greater tensile, impact, and ?exural strength than standard ABS. Layer bonding is signi?cantly stronger than that of standard ABS, for a more durable part. This results in more realistic functional tests and higher quality parts for end use. When combined with a Fortus 3D Production System, ABS-M30 gives you Real Parts that are stronger, smoother, and with better feature detail.

Available Colors: Ivory, White, Black, Dark Grey, Red, and Blue

Information provided by Proto3000 for their protoyping engineering services.

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	1.04 g/cc	0.0376 lb/in3	ASTM D792

机械性能	额定值 (公制)	额定值 (英制)	测试方法
洛氏硬度（R 级）	109.5	109.5	ASTM D785
抗张强度(断裂)	36.0 MPa	5220 psi	Type 1, 2"/min; ASTM D638
伸长率 (断裂)	4.0 %	4.0 %	ASTM D638
	52 %	52 %	Flexural Elongation; ASTM D790
拉伸模量	2.413 GPa	350.0 ksi	ASTM D638
弯曲强度	61.0 MPa	8850 psi	Method 1, 0.05"/min; ASTM D790
弯曲模量	2.317 GPa	336.1 ksi	ASTM D790
悬壁梁缺口冲击强度	1.39 J/cm	2.60 ft-lb/in	Method A; ASTM D256
悬壁梁无缺口冲击强度	2.83 J/cm	5.30 ft-lb/in	Method A; ASTM D256

电气性能	额定值 (公制)	额定值 (英制)	测试方法
介电强度	28.0 kV/mm	711 kV/in	IEC 60112

热性能	额定值 (公制)	额定值 (英制)	测试方法
线形热膨胀系数 - 流动	82.2 μm/m-°C @Temperature -40.0 - 100 °C	45.7 μin/in-°F @Temperature -40.0 - 212 °F	ASTM E831
线性热膨胀系数,横向流动	84.6 μm/m-°C @Temperature -40.0 - 100 °C	47.0 μin/in-°F @Temperature -40.0 - 212 °F	ASTM E831
载荷下热变形温度(0.46 MPa)	96.0 °C @Thickness 0.125 mm	205 °F @Thickness 0.00492 in	unannealed; ASTM D648
载荷下热变形温度(1.8 MPa)	82.0 °C @Thickness 0.125 mm	180 °F @Thickness 0.00492 in	unannealed; ASTM D648
维卡软化温度	99.0 °C	210 °F	Rate B/50; ASTM D1525
玻璃化转变温度，Tg	108 °C	226 °F	DAM (SSYS)
可燃性(UL94)	HB @Thickness 0.850 mm	HB @Thickness 0.0335 in