GEHR Plastics PPS Polyphenylene Sulfide

Polyphenylene Sulfide (PPS)

GEHR Plastics Inc

产品说明：

The linear polyphenylensulfide belongs to the semi-crystalline materials and offers a very high mechanical capacity, thermal and chemical resistance distinguished at the same time, high dimensional stability, and creep strength. The LOI belongs to the highest of polymers. By the reinforcement with glass polymers strength is achieved, which is comparable with light metal. PPS closes the gap between the technical synthetics and PEEK with its strength and economy.

Properties

• very high strength and rigidity
• high hardness
• high thermostability
• high dimensional stability
• very high chemical resistance
• very good insulating properties
• high weather resistance
• high resistance to hydrolysis

Applications include components in machine-making, pump parts, fan parts, impellers, parts in the fuel and automotive sector.

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	1.35 g/cc	1.35 g/cc	ISO 1183
吸水率	0.020 %	0.020 %	ISO 62

机械性能	额定值 (公制)	额定值 (英制)	测试方法
洛氏硬度（M 级）	95	95
抗张强度(断裂)	72.0 MPa	10400 psi	ISO 527
抗张强度(屈服)	88.0 MPa	12800 psi	ISO 527
伸长率 (断裂)	21 %	21 %	ISO 527
屈服伸长率	3.4 %	3.4 %	ISO 527
弹性模量	4.15 GPa	602 ksi	ISO 527
弯曲强度	141 MPa	20500 psi	3.5%; ISO 178
简支梁无缺口冲击强度	>= 25.0 J/cm2	>= 119 ft-lb/in2	ISO 179
摩擦系数	0.40	0.40	DIN 53375

电气性能	额定值 (公制)	额定值 (英制)	测试方法
体积电阻率	>= 1.00e+11 ohm-cm	>= 1.00e+11 ohm-cm	VDE 0303
表面电阻率	>= 1.00e+15 ohm	>= 1.00e+15 ohm	VDE 0303
介电常数	3.2 @Frequency 1.00e+6 Hz	3.2 @Frequency 1.00e+6 Hz	DIN 53483
介电强度	18.0 kV/mm	457 kV/in	VDE 0303
相比耐漏电起痕指数(CTI)	125 V	125 V	CTI; IEC 60112

热性能	额定值 (公制)	额定值 (英制)	测试方法
线性热膨胀系数	53.0 μm/m-°C @Temperature 20.0 °C	29.4 μin/in-°F @Temperature 68.0 °F	DIN 53752
导热系数	0.250 W/m-K	1.74 BTU-in/hr-ft2-°F	DIN 52612
工作温度, Air	150 °C	302 °F
载荷下热变形温度(1.8 MPa)	115 °C	239 °F	ISO 75
可燃性(UL94)	V-0	V-0

材料描述		测试方法
Acid Resistance	yes
Aromatic Resistance	limited
Bondability	yes
CKW Resistance	yes
颜色	Natural
Hydrocarbonate Resistance	yes
Hydroxide Resistance	limited
Ketone Resistance	yes
Physiological indifference according	yes
Resistance Against Hot Water	yes
UV Stabilization	yes