Toyobo TS301 PPS, 30% Glass Fiber Reinforced

Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler

Toyobo

产品说明：

Key Feature: Excellent impact resistance, high flow

High performance injection-molding resin created from crystalline polyphenylene sulfide, using a special formulation technology developed by Toyobo. Excellent physical, electrical, and thermal properties, corrosion resistant, and inherently flame retardant. PPS resins are used in the electrical, electronic, automotive, and industrial machinery industries.

Information provided by Toyobo Co., Ltd

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	1.55 g/cc	0.0560 lb/in3	ASTM D792
吸水率	0.030 %	0.030 %	24 hrs; ASTM D570
线性成型收缩率	0.0030 cm/cm	0.0030 in/in
线性成型收缩率，横向	0.0095 cm/cm	0.0095 in/in

机械性能	额定值 (公制)	额定值 (英制)	测试方法
洛氏硬度（R 级）	120	120	ASTM D785
极限抗拉强度	157 MPa	22800 psi	ASMT D638
伸长率 (断裂)	1.8 %	1.8 %	ASTM D638
弹性模量	10.8 GPa	1570 ksi	ASMT D638
弯曲强度	206 MPa	29900 psi	Flexural elongation is 2.1%; ASTM D790
弯曲模量	9.80 GPa	1420 ksi	ASMT D790
悬壁梁缺口冲击强度	1.60 J/cm	3.00 ft-lb/in	ASTM D256

电气性能	额定值 (公制)	额定值 (英制)	测试方法
电阻率	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
介电常数	3.9 @Frequency 1e+6 Hz	3.9 @Frequency 1e+6 Hz	ASTM D150
	4.0 @Frequency 1000 Hz	4.0 @Frequency 1000 Hz	ASTM D150
介电强度	13.0 kV/mm	330 kV/in	ASTM D149
耗散因数	0.0013 @Frequency 1e+6 Hz	0.0013 @Frequency 1e+6 Hz	ASTM D150
	0.0016 @Frequency 1000 Hz	0.0016 @Frequency 1000 Hz	ASTM D150
耐电弧性	97 sec	97 sec	ASTM D495
相比耐漏电起痕指数(CTI)	155 V	155 V	IEC test

热性能	额定值 (公制)	额定值 (英制)	测试方法
线性热膨胀系数	9.00 μm/m-°C @Temperature 20.0 °C	5.00 μin/in-°F @Temperature 68.0 °F	MD
线性热膨胀系数,横向流动	69.0 μm/m-°C @Temperature 20.0 °C	38.3 μin/in-°F @Temperature 68.0 °F
熔融温度	282 °C	540 °F
载荷下热变形温度(1.8 MPa)	>= 260 °C	>= 500 °F	ASTM D648
可燃性(UL94)	V-0	V-0